The wire rope for hoisting with various constructions of multi-layer, linear and facial contacted structure can meet the demand in cranes, harbor and metallurgy.
Norminal diameter | ApproxWeight | NominalStrength MPa | ||||
1570 | 1670 | 1770 | 1870 | 1970 | ||
Min.Breaking Load kN | ||||||
8 10 12 13 14 16 18 20 22 24 26 28 30 32 34 36 38 40 42 44 46 48 50 52 54 56 58 60 | 26.8 41.8 60.2 70.6 81.9 107 135 167 202 241 283 328 376 428 483 542 604 669 737 809 884 963 1040 1130 1220 1310 1410 1500 | 35.8 55.9 80.5 94.5 110 143 181 224 271 322 378 438 503 572 646 724 807 894 986 1080 1180 1290 1400 1510 1630 1750 1880 2010 | 38.0 59.5 85.6 100 117 152 193 238 288 342 402 466 535 609 687 770 858 951 1050 1150 1260 1370 1490 1610 1730 1860 2000 2140 | 40.3 63.0 90.7 106 124 161 204 252 305 363 426 494 567 645 728 817 910 1010 1110 1220 1330 1450 1580 1700 1840 1980 2120 2270 | 42.6 66.6 95.6 113 130 170 216 266 322 383 450 522 599 682 770 863 961 1070 1170 1290 1410 1530 1660 1800 1940 2090 2240 2400 | 44.7 69.8 100 118 137 179 226 279 338 402 472 547 628 715 807 904 1010 1120 1230 1350 1480 1610 1740 1890 2030 2190 2350 2510 |
Note:The total Min.breakingload=Min.breaking load X1.321(steel core) |
Norminal diameter | ApproxWeight | NominalStrength MPa | |||
1570 | 1670 | 1770 | 1870 | ||
Min.Breaking Load kN | |||||
16 18 20 22 24 26 28 30 32 34 36 38 40 42 44 46 48 50 52 54 56 58 60 | 122 155 191 231 275 322 374 429 488 551 618 689 763 841 923 1010 1100 1190 1290 1390 1500 1600 1720 | 165 209 257 312 371 435 505 579 659 744 834 930 1030 1140 1250 1360 1480 1610 1740 1880 2020 217 2320 | 175 222 274 331 394 463 537 616 701 792 887 989 1100 1210 1330 1450 1580 1710 1850 2000 2150 2300 2460 | 186 235 290 351 418 491 569 653 743 839 941 1050 1160 1280 1400 1540 1670 1810 1960 2120 2280 2440 2610 | 196 248 307 371 442 518 601 690 785 886 994 1110 1230 1350 1480 1620 1770 1920 2070 2240 2400 2580 2760 |
Note:The total Min.breakingload=Min.breaking load X 1.321 |
Norminal diameter | ApproxWeight | NominalStrength MPa | |||
1570 | 1670 | 1770 | 1870 | ||
Min.Breaking Load kN | |||||
18 20 22 24 26 28 30 32 34 36 38 40 42 44 46 48 50 52 54 56 58 60 62 64 66 68 70 | 160 198 240 285 335 388 446 507 572 642 715 792 873 958 1050 1140 1240 1340 1440 1550 1670 1780 1900 2030 2160 2290 2430 | 209 257 312 371 435 505 579 659 744 834 930 1030 1140 1250 1360 1480 1610 1740 1880 2020 2170 2320 2470 2640 2800 2980 3150 | 222 274 331 394 463 537 616 701 792 887 989 1100 1210 1330 1450 1580 1710 1850 2000 2150 2300 2460 2630 2800 2980 3170 3360 | 235 290 351 418 491 569 653 743 839 941 1050 1160 1280 1400 1540 1670 1810 1960 2120 2280 2440 2610 2790 2970 3160 3360 3560 | 248 307 371 442 518 601 690 785 886 994 1110 1230 1350 1480 1620 1770 1920 2070 2240 2400 2580 2760 2950 3140 3340 3550 3760 |
Note:The total Min.breakingload=Min.breaking load X 1.374 |
Norminal diameter | ApproxWeight | NominalStrength MPa | ||||
1570 | 1670 | 1770 | 1870 | 1960 | ||
Min.Breaking Load kN | ||||||
20 | 204
| 257 312 371 435 505 579 659 744 834 930 1030 1140 1250 1360 1480 1610 1740 1880 2020 2170 2320 | 274
| 290 351 418 491 569 653 743 839 941 1050 1160 1280 1400 1540 1670 1810 1960 2120 2280 2440 2610 | 307 371 442 518 601 690 785 886 994 1110 1230 1350 1480 1620 1770 1920 2070 2240 2400 2580 2760 | 321 389 463 543 630 723 823 929 1040 1160 1290 1420 1560 1700 1850 2010 2170 2340 2520 2700 2890 |
Note:The total Min.breakingload=Min.breaking load X 1.287 |